The result indicates that the improvement of the fatigue limit is due to the nano-crystallization and severe plastic deformation in the surface layer induced by high-energy shot peening.

• 结果表明,高能喷丸后其表层组织发生严重塑性变形并实现组织纳米化,是提高弯曲疲劳寿命的主要原因。