The increases of vacancy defects might be that the extension of structures of porous silicon towards inner layer with anodization time and caused more vacancy defects in inner layer.

• 空位缺陷增多的原因可能是随着阳极氧化时间的延长，多孔硅结构向内层延伸增加了空位缺陷。