您要查找的是不是：
- Intergranular stress corrosion cracking behavior of austenitic steels on hydrogenated high-temperature. 奥氏体钢在高温氢化物中的晶间应力腐蚀开裂性能。
- The intergranular stress corrosion cracking(SCC) problem in steel shells on hightemperature blast furnace stoves was investigated in this paper. 以高风温热风炉的沿晶应力腐蚀断裂问题为背景，研究了低合金钢在硝酸盐溶液体系中的应力腐蚀行为。
- Experimental study on intergranular stress corrosion of stainless steelused in glycol evaporators 乙二醇不锈钢蒸发器晶间应力腐蚀的试验研究
- Keywords Stainless steel;Evaporator;Intergranular stress corrosion cracking;Finite element simulation;Misalignment stress;Safety analysis; 不锈钢;蒸发器;晶间应力腐蚀开裂;有限元模拟;装配应力;安全分析;
- Keywords Stainless steel evaporator;Remanufacture technology;Intergranular stress corrosion cracking;Finite element simulation;Welding residual stress;Safety assessment; 不锈钢蒸发器;再制造技术;晶间应力腐蚀开裂;有限元模拟;焊接残余应力;安全评价;
- intergranular stress corrosion 晶间型应力腐蚀
- This metal defect is known as stress corrosion cracking. 其金属缺陷就称为应力锈蚀腐蚀裂纹。
- The coupling agent may protect the interface against stress corrosion by water. 偶联剂可保护界面免受水的应力侵蚀。
- Many studies in the related area of stress corrosion or subcritical crack growth use simplified test systems. 许多有关应力腐蚀或亚临界裂纹发展领域的研究使用了简化的试验系统。
- The problem of serious stress corrosion existed in sour water tank in sour water striping unit of sulphur workshop was analyzed. 对硫磺车间的酸性水汽提装置中的酸性水罐存在的严重应力腐蚀问题进行了分析。
- Carbon steel -- Very good mechanical properties; good resistance to stress corrosion and sulfides. 碳钢--具有很好的机械特性;良好的抗金属超应力腐蚀的能力和抗硫化物腐蚀的能力。
- The analysis results indicated that the H_2S in the LPG caused sulfide stress corrosion cracking (SSCC) of the flange. 分析结果表明,法兰断裂是由液化气中的H2S所引起的应力腐蚀开裂。
- The analysis results indicated that the H2S in the LPG caused sulfide stress corrosion cracking (SSCC) of the flange. 分析结果表明，法兰断裂是由液化气中的H2S所引起的应力腐蚀并裂。
- The results indicate that the cracks on the wainscot of gasoline tank were stress corrosion cracks. 两批油箱壁板在加工完成后,放置一段时间后出现裂纹。
- The results show that the cracking of the pipe is a kind of stress corrosion cracking (SCC). 分析结果表明，高压油管的开裂是应力腐蚀开裂造成的。
- Stress corrosion manifests itself as a crack in the metal not necessary accompanied by obvious corrosion. 应力锈蚀腐蚀会显现出金属裂纹而不一定会有明显的锈蚀腐蚀。
- Stress corrosion cracking occurs in both aluminum and magnesium alloys as well as steel. 铝和镁合金以及钢都会发生应力锈蚀腐蚀的破裂。
- Relationship between yield strength and near-neutral pH stress corrosion cracking resistance of pipeline steels-an effect of microstructure. 管道钢的屈服强度和抗近中性pH应力腐蚀开裂间的关系-显微结构的影响。
- Commonly used as stem material in pressure-rated valves, silicon bronze has greater resistance to stress corrosion cracking than common brasses. 通常用作额定压力阀门的阀杆材料的硅青铜比普通黄铜具有更好的抗应力腐蚀裂纹的性能。
- Regression and Re-aging(RRA) can get super strengthness and preferable stress corrosion resistanee,but its fracure toughness is low. 回归再时效工艺可以获得最高的强度和较好的抗应力腐蚀性能，但其断裂韧性较差。