The increase in FCGR at a lower frequency at 500oC was thought to be caused by a time-dependent, oxidation-assisted cracking mechanism.

• 此频率效应是由裂缝尖端氧化与循环负载的加乘作用所造成，频率越低，则氧化的加乘效果越明显。