The high temperature near-solvus pre-precipitation following higher temperature solution treatment were performed on LC52 and Quansi 7039 aluminum alloy.

• 研究了高温固溶后降温处理工艺对中强可使预析出LC52和7039铝合金的组织、时效硬化和应力腐蚀的影响。